2K-Deripox Lack EE 30

Technical Specification
2K-Deripox Lack EE 30

Colours	RAL 5010, RAL-colour chart with exceptions, apart from RAL 9006/9007. Other colours upon request. Colour deviation (Colour deviations may occur in the range of high temperatures due to the restricted temperature resistance of the pigments)
Flash point	>23 °C
Temperature stability	-40 up to 200 °C
Gloss	Silky mat, appr. 20 U in 60° angle
Potential dry film thickness in one working process	60 up to 100 µm
Mixing ratio	Hardener HL 500	Hardener HL 510 (winter hardener)
(Basis:hardener) by weight	6:1	7:1
(Basis:hardener) by volume	5:1	4,5:1
Pot life in hours	8	3
Viscosity	Thixotrope	Thixotrope
Density in kg/l	1,34	1,36
Solid content in %	72	73
Solid volume in %	56	57
Theoretical spreading capacity	7 m²/l at 80 µm DFT 5,22 m²/kg at 80 µm DFT	7,13 m²/l at 80 µm DFT 5,24 m²/kg at 80 µm DFT
Recommended film thickness	150 µm WFT corresponds to 80 µm DFT	150 µm WFT corresponds to 90 µm DFT
Drying (DIN EN ISO 1517)	80 µm DFT	80 µm DFT
Dust-dry (Tg1)	After 50 min	After 20 min
Touch-dry (Tg4)	After 3 h	After 90 min
Dry (Tg6)	After 5 h	After 3 h
Cured chemically	After 7 days	After 4 days
Interval for overcoating	after 6 h with itself	after 3 h with itself

Note

• The specifications are related to the prepared mixture and are based on standard atmospheric conditions 23/50, DIN 50014.
• Lower temperatures and/or higher humidity will prolong drying and hardening.
• Application below +5 °C is not possible.
• Using winter quality application is possible nearly to frost temperature. Application only on steel supports possible.

Safety information
2K-Deripox Lack EE 30

(See Security Data Sheet)

VOC-level	Appr. 370 g/l
Solvent content	Appr. 28 % by weight	Appr. 27 % by weight
Aromatic content	Appr. 21 % by weight

Storage
2K-Deripox Lack EE 30

Storage

• In dry, cool rooms, if possible frost-proof
• Ensure good ventilation

Shelf life

• 6 month from date of delivery when in unopened original containers in cool and dry conditions

Application methods
2K-Deripox Lack EE 30

Mixing ratio

• Stirr homogeneous, preferably with mechanical stirrer
• Mix base paint and hardener according to the mixing ratio as specified

Airless spraying

• Flow pressure 180 - 200 bar
• Nozzle size 0,013 - 0,015 inch (0,33 - 0,38 mm)
• Spraying angle according to the geometry and size of the object to be laquered
• If required (two component: after mixing) using 5% Deripox-Verdünnung is possible

Compressed air spraying

• Spraying pressure 5 - 6 bar
• Nozzle size 1,5 - 2 mm
• Adjust to spraying viscosity (appr. 30 s DIN 4 mm) adding appr. 10 % Deripox-Verdünnung (two component products: after mixing)

Electrostatic application

• Application is possible provided that the material is diluted

Dipping

• Can not be applied as delivered

Other methods

• Roller and brush application is possible in the quality as delivered

Thinner

• Max. 15% Deripox-Verdünnung

Cleaning

• Rinse immediately with Deripox-Verdünnung

Preparation of support

• Shot blasting to a purity according to SA 2½
• If necessary clean with high pressure-cleaner and turbo-cleaner-solution
• Sweeping for zinced supports
• Mill scale, welding residues, dust, soluble residues from chemical pretreatments and zinc reaction products which might reduce adhesion have to be carefully and thoroughly removed

General remarks

• During coating and drying the humidity should be min. 10 % / max. 85 %
• During coating and drying the environmental temperature should be min. 5°C / max. 30°C
• Object temperature at least 3° C above dew point.

Example for a system

• Primer coat: 2K-Deripox Grund 60 HS
• Finish coat: 2K-Deripox Lack EE 30