Derilux EPE 60
Top coat on epoxy-ester resin basis with aluminum pigments
General information
Derilux EPE 60
Field of application
- Protectionsystems against corrosion for iron and steel with high temperatures.
- Adhesion on aluminium and zinced supports.
- Agree with VOC directive for one-pack performance coatings.
Product properties
- Silicon-free
- Resistance to mineral oils
- Good elasticity
Technical Specification
Derilux EPE 60
| Colours |
RAL 9006.
Colour deviation (Colour deviations may occur in the range of high temperatures due to the restricted temperature resistance of the pigments) |
|---|---|
| Flash point | >23 °C |
| Temperature stability | -20 up to 200 °C |
| Gloss | Satin glossy |
| Potential dry film thickness in one working process | 40 up to 50 µm |
| Viscosity | Thixotrope |
| Density in kg/l | 0,98 |
| Solid content in % | 41 |
| Solid volume in % | 34 |
| Theoretical spreading capacity |
|
| Recommended film thickness | 125 µm WFT corresponds to 40 µm DFT |
| Drying (DIN EN ISO 1517) | 40 µm DFT |
| Dust-dry (Tg1) | After 40 min |
| Touch-dry (Tg4) | After 150 min |
| Dry (Tg6) | After 48 h |
| Cured chemically | After 7 days |
Note
- The specifications are based on standard atmospheric conditions 23/50, DIN 50014.
- Lower temperatures and/or higher humidity will prolong drying and hardening.
Safety information
Derilux EPE 60
(See Security Data Sheet)
| VOC-level | Appr. 576 g/l |
|---|---|
| Solvent content | Appr. 59 % by weight |
| Aromatic content | Appr. 56 % by weight |
Storage
Derilux EPE 60
Storage
- In dry, cool rooms, if possible frost-proof
- Ensure good ventilation
Shelf life
- 6 month from date of delivery when in unopened original containers in cool and dry conditions
Application methods
Derilux EPE 60
Airless spraying
- Flow pressure 150 - 180 bar
- Nozzle size 0,011 inch (0,28 mm)
- Spraying angle according to the geometry and size of the object to be laquered
Compressed air spraying
- Spraying pressure 5 - 6 bar
- Nozzle size 1,2 - 1,6 mm
- Adjust to spraying viscosity (appr. 30 s DIN 4 mm) adding appr. 5 % Derozink-Verdünnung (two component products: after mixing)
Electrostatic application
- Application is not possible
Dipping
- Can not be applied as delivered
Other methods
- Roller and brush application for repair work is possible
Thinner
- Max. 10% Derozink-Verdünnung
Cleaning
- Rinse immediately with Derozink-Verdünnung
- Residues are dissolvable with Derozink-Verdünnung
Preparation of support
- Shot blasting to a purity according to SA 2½
- Mill scale, welding residues, dust, soluble residues from chemical pretreatments and zinc reaction products which might reduce adhesion have to be carefully and thoroughly removed
- Clean primer of the coating system
General remarks
- During coating and drying the humidity should be min. 10 % / max. 85 %
- During coating and drying the environmental temperature should be min. 5°C / max. 30°C
- Object temperature at least 3° C above dew point.
Example for a system
- Primer coat: Derogrund EPE
- Intermediate coat:
- Finish coat: Derilux EPE 60
The general information and descriptions contained in this specification are provided to the best of our knowledge. Our information and specifications do not constitute warranted characteristics in the legal sense. Any advice for preparation and application which may be provided verbally, in writing or by means of experiments is of general nature only, and any property rights of third parties are also to be regarded in this context. Our general instructions do not release you from your obligation to check the suitability of the products supplied by our company for the intended methods and purposes of application. Particular in those cases when our supplied material will be applied with products from other sources. The products are prepared, applied and used outside of our sphere of control and thus fall solely within the user´s scope of responsibility.