2K-Deripox Protec EG

Technical Specification
2K-Deripox Protec EG

Colours	DB 702. Other colours upon request.
Flash point	>23 °C
Temperature stability	-40 up to 200 °C
Gloss	Silky mat
Potential dry film thickness in one working process	80 up to 160 µm
Mixing ratio	Hardener HL 560
(Basis:hardener) by weight	9:1
(Basis:hardener) by volume	4,5:1
Pot life in hours	2
Viscosity	Thixotrope
Density in kg/l	1,8
Solid content in %	82
Solid volume in %	62
Theoretical spreading capacity	7,75 m²/l at 80 µm DFT 4,31 m²/kg at 80 µm DFT
Recommended film thickness	125 µm WFT corresponds to 80 µm DFT
Drying (DIN EN ISO 1517)	80 µm DFT
Dust-dry (Tg1)	After 30 min
Touch-dry (Tg4)	After 2 h
Dry (Tg6)	After 3 h
Cured chemically	After 7 days
Interval for overcoating	after 3 h with two component topcoats

Note

• The specifications are related to the prepared mixture and are based on standard atmospheric conditions 23/50, DIN 50014.
• Lower temperatures and/or higher humidity will prolong drying and hardening.
• It is possible to use this material to limit frost temperature (possibly solvents are necessary).

Safety information
2K-Deripox Protec EG

(See Security Data Sheet)

VOC-level	Appr. 284 g/l
Solvent content	Appr. 17 % by weight
Aromatic content	Appr. 13 % by weight

Storage
2K-Deripox Protec EG

Storage

• In dry, cool rooms, if possible frost-proof
• Ensure good ventilation

Shelf life

• 6 month from date of delivery when in unopened original containers in cool and dry conditions

Application methods
2K-Deripox Protec EG

Mixing ratio

• Stirr homogeneous, preferably with mechanical stirrer
• Mix base paint and hardener according to the mixing ratio as specified

Airless spraying

• Flow pressure 180 bar
• Nozzle size 0,015 - 0,019 inch (0,38 - 0,48 mm)
• Spraying angle according to the geometry and size of the object to be laquered

Compressed air spraying

• Spraying pressure 5 - 6 bar
• Nozzle size 1,6 - 1,8 mm
• Adjust to spraying viscosity (appr. 60 s DIN 4 mm) adding appr. 10 % Deripox-Verdünnung (two component products: after mixing)

Electrostatic application

• Application is possible provided that the material is diluted

Dipping

• Can not be applied as delivered

Other methods

• Roller and brush application is possible in the quality as delivered

Thinner

• Max. 10% Deripox-Verdünnung

Cleaning

• Rinse immediately with Deripox-Verdünnung

Preparation of support

• Shot blasting to a purity according to SA 2½
• Sweeping for zinced supports
• Mill scale, welding residues, dust and dirt on the surface which might reduce adhesion have to be carefully and thoroughly removed

General remarks

• During coating and drying the humidity should be min. 30 % / max. 85 %
• During coating and drying the environmental temperature should be min. 5°C / max. 30°C
• Object temperature at least 3° C above dew point.

Example for a system

• Primer coat: 2K-Deripox Protec ZP
• Intermediate coat: 2K-Deripox Protec EG
• Finish coat: 2K-Derocryl Lack 80 HS