Derocryl Grund Hydro GT

Water borne adhesion-primer on an acrylat dispersion basis.

General information
Derocryl Grund Hydro GT

Field of application

  • Adhesion primer for aluminium, galvanized and stainless steel substrates.
  • Meets the requirements for quality levels 1-4 in the DGNB system. Can also be used for corrosion protection on steel. A variant with mica is available for special requirements.

Product properties

  • Free from aromatic compounds
  • Water based
  • Resistance to condensation
  • Coating systems for corrosivity category C3
  • Fast drying
  • Fast recoatability
  • Primer: universal

Technical Specification
Derocryl Grund Hydro GT

Colours ca. RAL 7040, light-grey, white.
Flash point Not applicable
Temperature stability Up to 120 (short-term up to 150) °C
Gloss Mat
Potential dry film thickness in one working process 60 up to 100 µm
Viscosity Thixotrope
Density in kg/l 1,38
Solid content in % 64
Solid volume in % 50
Theoretical spreading capacity
  • 6,25 m²/l at 80 µm DFT
  • 4,53 m²/kg at 80 µm DFT
Recommended film thickness 150 µm WFT corresponds to 80 µm DFT
Drying (DIN EN ISO 1517) 80 µm DFT
Dust-dry (Tg1) After 30 min
Touch-dry (Tg4) After 60 min
Dry (Tg6) After 2 h
Accelerated drying 30 min. at 60°C possible, after 10 min. flash-off time
Interval for overcoating
  • after 2 h with water based topcoats
  • after 4 h with single-component topcoats
  • after 4 h with two component Derocryl topcoats

Note

  • The specifications are based on standard atmospheric conditions 23/50, DIN 50014.
  • Lower temperatures and/or higher humidity will prolong drying and hardening.

Safety information
Derocryl Grund Hydro GT

(See Security Data Sheet)

Solvent content Appr. 2 % by weight

Storage
Derocryl Grund Hydro GT

Storage

  • In dry, cool rooms, frost-proof
  • Ensure good ventilation

Shelf life

  • 6 month from date of delivery when in unopened original containers in cool and dry conditions

Application methods
Derocryl Grund Hydro GT

Airless spraying

  • Risk of spray dust due to very fast drying
  • After using the material close the packings immediately
  • Dip the pistol and the nozzle into water during the breaks
  • It is tending to fast skinning. Do not stir the skin in any case!
  • Flow pressure 90 - 100 bar
  • Nozzle size 0,011 - 0,013 inch (0,28 - 0,33 mm)
  • Spraying angle according to the geometry and size of the object to be laquered

Compressed air spraying

  • Spraying pressure 3 - 4 bar
  • Nozzle size 1,3 - 1,6 mm
  • Adjust to spraying viscosity (appr. 80 s DIN 4 mm) adding appr. 5 % Water (two component products: after mixing)

Electrostatic application

  • Application is possible, provided the equipment is suitable for water based materials

Dipping

  • Can not be applied as delivered

Other methods

  • Roller and brush application is possible in the quality as delivered
  • Double application is possible in viscosity as delivered

Thinner

  • Max. 5% Water

Cleaning

  • Rinse immediately with Water
  • Residues are dissolvable with Deripox-Verdünnung

Preparation of support

  • Shot blasting to a purity according to SA 2½
  • Sweeping for zinced supports
  • Mill scale, welding residues, dust, soluble residues from chemical pretreatments and zinc reaction products which might reduce adhesion have to be carefully and thoroughly removed
  • Cleaning with alkaline wetting agent

General remarks

  • During coating and drying the humidity should be min. 30 % / max. 85 %
  • During coating and drying the environmental temperature should be min. 5°C / max. 30°C
  • Object temperature at least 3° C above dew point.

Example for a system

  • Primer coat: Derocryl Grund Hydro GT
  • Finish coat: 2K-DC Lack 70 ST Biobased

Derisol Hydro Shopprimer

Newest Shopprimer Generation

Shopprimer Hydro EcoWeld

2K-Hydropox Shopprimer

See the products

2K-Derocryl Lack AgriFlex

ACE- Agriculture Construction Earthmoving Equipment

High Gloss DTM High Solid. Excellent corrosion protection at 60 µm DFT.

Product Information

2K-Derocryl Lack DTM Rapid

HS One layer coat with extremly fast drying at high layer thicknesses

Two component coat on acryl resin. Economic coating system for steel

See more details

The general information and descriptions contained in this specification are provided to the best of our knowledge. Our information and specifications do not constitute warranted characteristics in the legal sense. Any advice for preparation and application which may be provided verbally, in writing or by means of experiments is of general nature only, and any property rights of third parties are also to be regarded in this context. Our general instructions do not release you from your obligation to check the suitability of the products supplied by our company for the intended methods and purposes of application. Particular in those cases when our supplied material will be applied with products from other sources. The products are prepared, applied and used outside of our sphere of control and thus fall solely within the user´s scope of responsibility.
Our general terms of sale and delivery apply as agreed.

Quick access to product information.

Dr. Demuth Derisol Lackfarben GmbH & Co. KG

Hillerser Straße 8, 37154 Northeim
Telefon +49 5551 / 97940
Telefax +49 5551 / 979430

Cookie Settings

We use cookies to improve your experience and to provide you with personalized content. By using this website you agree to our cookie policy

Necessary Cookies
Statistical Cookies
Third-party Cookies
Accept Change Settings
www.dr-demuth.com

Cookie Settings

More information on how we use cookies in our cookie policy.

­

Necessary Cookies

Without these Cookies services you have asked for cannot be provided.

Statistical Cookies

Allow anonymous usage statistics so that we can improve our offering.

Third-party Cookies

Third-party cookies that are integrated to deliver personalized ads for you.

Cookies We use on This Site